Stainless Steels
Ferritic
Main features of TDS-J:
(1) Electromagnetic Stainless SteelShielding Cases, Electromagnetic Shields
Thickness
Please contact us.
Width
3.0-300mm
Length
COIL or SHEET less than 2000mm
This is the manufacturing range of coils and sheets we manufacture.
Density
7.74 g/cm³
Specific Heat
440 J/(kg・K)(25℃)
Electrical Resistivity
58 μΩ・cm
Young's Modulus
204 GPa
Thermal Expansion
10.5×10-6/K(20~100℃)
Thermal Conductivity
22.5 W/(m・K)
Melting Range
1460-1500 ℃
Magnetism
Soft Magnetism
It has mechanical properties equivalent to SUS430. Detailed condition is to be disucussed later.
It has corrosion resistance equivalent to SUS304 with higher Cr content and added Cu and Ti which contribute to corrosion resistance.
It has higher corrosion resistance than SUS430, soft magnetic iron steels, and permalloy and in general environments, it can be used without plating or other surface treatment.
The results of the salt spray test is shown in the figure below and there is no rust forming as well as SUS304.
The table below shows the comparison of magnetic properties of TDS-J and SUS430.
*Values are representative values obtained by VSM (vibrating sample magnetometer).
It has better maximum permeability and coercive force than SUS430, resulting in a high response to external magnetic fields.
Soft magnetic material is easily magnetized when a magnetic field is applied, but returns to its original state when the magnetic field is removed. We also manufacture our original steel grades such as electromagnetic stainless steel with corrosion resistance and extremely high strength.
Stainless steel is an alloy of iron (Fe) with at least 10.5% chromium (Cr) and is used in a wide range of applications because it has good properties in terms of corrosion resistance, strength, workability, and heat resistance.